Building components- external wall - awropi11a
 
 


Cross-section of standard configuration
[Additional views]

Last update23.03.2017/hfa.plb
external wall: timber frame construction, not ventilated, with dry lining, with rendering

register of building materials used for this application, cross-section
(from outside to inside, dimensions in mm)

  Thickness Building material  λ   μ min - max   ρ   c  Reaction to fire
EN
 4.0 plaster   1,000  10 - 35  2000  1,130   A1
 50.0 wood wool composite boards   0,090  2 - 5  370  2,000   B
 15.0 fibreboard (MDF)   0,120  11  600  1,700   D
*   finger-jointed solid construction timber (60/..; e=*)  0,120  50  450  1,600   D
*   Insulation material            
 15.0 OSB (sealed with airtight tape)  0,130  200  650  1,700   D
*   spruce wood cross battens (a=400) or battens offset)  0,120  50  450  1,600   D
*   Insulation materialor air layer in type 02            
 12.5 gypsum plasterboards with improved properties at high temperatures (fire) or  0,250  10  800  1,050   A2
 12.5 gypsum fibre board   0,320  21  1000  1,100   A2
   
               
  Variations of building components

No. Thickness of layer Note Fire performance Thermal performance Acoustic performance Eco Sustainability Mass HTMLPDF
  D* E* G* H* Σ   REI U [W/(m²K)] mw,B,A [kg/m²] Diffusion Ln,w(Cl) Rw(C,Ctr) OI3Kon m [kg/m²]   
00   160,0  160,0  40,0  40,0  296,5  e=625
 
60  0,19  19,8  adequate  –  52(-3,-8)  6,9  65,6   awropi11a-00  
E/H = glass wool [0,0040; R=16]
01   120,0  120,0  40,0  40,0  256,5  e=625
 
60  0,23  19,5  adequate  –  51(-3,-8)  4,3  63,1   awropi11a-01  
E/H = glass wool [0,0040; R=16]
02   160,0  160,0  40,0    296,5  e=625 ; I=without insulation
 
60  0,22  28,6  adequate  –  51(-3,-8)  4,6  65,1   awropi11a-02  
E = glass wool [0,0040; R=16]
03   200,0  200,0  40,0  40,0  336,5  e=625
 
60  0,16  19,9  adequate  –  53(-3,-8)  9,4  68,1   awropi11a-03  
E/H = glass wool [0,0040; R=16]
04   240,0  240,0  40,0  40,0  376,5  e=625
 
60  0,14  20,0  adequate  –  54(-3,-8)  11,9  70,6   awropi11a-04  
E/H = glass wool [0,0040; R=16]
05   200,0  200,0  80,0  80,0  376,5  e=625
 
60  0,14  16,5  adequate  –  53(-3,-8)  11,6  71,2   awropi11a-05  
E/H = glass wool [0,0040; R=16]
06   240,0  240,0  80,0  80,0  416,5  e=625
 
60  0,13  16,6  adequate  –  54(-3,-8)  14,2  73,7   awropi11a-06  
E/H = glass wool [0,0040; R=16]
07   160,0  160,0  40,0  40,0  296,5  e=625
 
60  0,17  19,1  adequate  –  53(-3,-8)  32,2  71,7   awropi11a-07  
E/H = glass wool [0,0035; R=50]
08   160,0  160,0  40,0  40,0  296,5  e=625
 
60  0,19  19,8  adequate  –  52(-3,-8)  9,4  68,7   awropi11a-08  
E/H = mineral wool [0,038; R=33]
09   160,0  160,0  40,0  40,0  296,5  e=625
 
60  0,19  19,8  adequate  –  52(-3,-8)  0,2  72,6   awropi11a-09  
E = cellulose fibre [040; E]
10   160,0  160,0  40,0  40,0  296,5  e=625
 
60  0,21  21,0  adequate  –  52(-3,-8)  -2,0  66,1   awropi11a-10  
E/H = sheep wool [0,041; R=26]
11   160,0  160,0  40,0  40,0  296,5  e=400
 
60  0,20  19,7  adequate  –  52(-3,-8)  6,5  69,8   awropi11a-11  
E/H = glass wool [0,0040; R=16]