Building components- external wall - awropo11a
 
 


Cross-section of standard configuration
[Additional views]

Last update23.03.2017/hfa.plb
external wall: timber frame construction, not ventilated, without dry lining, with rendering

register of building materials used for this application, cross-section
(from outside to inside, dimensions in mm)

  Thickness Building material  λ   μ min - max   ρ   c  Reaction to fire
EN
 4.0 plaster   1,000  10 - 35  2000  1,130   A1
*   Exchangeable layer          
 25.0 spruce wood closed cladding without spacing of cladding boards  0,120  50  450  1,600   D
*   finger-jointed solid construction timber (60/160; e=*)  0,120  50  450  1,600   D
*   Insulation material            
 25.0 spruce wood closed cladding without spacing of cladding boards  0,120  50  450  1,600   D
  vapour barrier sd≥ 16m       1000     
 12.5 gypsum plasterboards with improved properties at high temperatures (fire) or  0,250  10  800  1,050   A2
 12.5 gypsum fibre board   0,320  21  1000  1,100   A2
   
               
  Variations of building components

No. Thickness of layer Note Fire performance Thermal performance Acoustic performance Eco Sustainability Mass HTMLPDF
  B* D* E* Σ   REI U [W/(m²K)] mw,B,A [kg/m²] Diffusion Ln,w(Cl) Rw(C,Ctr) OI3Kon m [kg/m²]   
00   50,0  160,0  160,0  276,5  e=625
B=Polystyrene EPS-F [0,040] 
60  0,19  29,4  adequate  –  44(-2,-6)  -5,5  52,8   awropo11a-00  
E = glass wool [0,0040; R=16]
01   50,0  120,0  120,0  236,5  e=625
B=Polystyrene EPS-F [0,040] 
60  0,23  29,4  adequate  –  43(-2,-6)  -8,0  50,3   awropo11a-01  
E = glass wool [0,0040; R=16]
02   50,0  200,0  200,0  316,5  e=625
B=Polystyrene EPS-F [0,040] 
60  0,16  29,4  adequate  –  45(-2,-6)  -3,0  55,3   awropo11a-02  
E = glass wool [0,0040; R=16]
03   50,0  240,0  240,0  356,5  e=625
B=Polystyrene EPS-F [0,040] 
60  0,14  29,4  adequate  –  46(-2,-6)  -0,5  57,8   awropo11a-03  
E = glass wool [0,0040; R=16]
04   50,0  160,0  160,0  276,5  e=625
B=Polystyrene EPS-F [0,040] 
60  0,18  29,4  adequate  –  45(-2,-6)  15,0  57,8   awropo11a-04  
E = glass wool [0,0035; R=50]
05   50,0  160,0  160,0  276,5  e=625
B=Polystyrene EPS-F [0,040] 
60  0,19  29,4  adequate  –  44(-2,-6)  -3,5  55,2   awropo11a-05  
E = mineral wool [0,038; R=33]
06   50,0  160,0  160,0  276,5  e=625
B=Polystyrene EPS-F [0,040] 
60  0,19  29,4  adequate  –  44(-2,-6)  -10,9  61,3   awropo11a-06  
E = cellulose fibre [0,040; R=55]
07   50,0  160,0  160,0  276,5  e=625
B=Polystyrene EPS-F [0,040] 
60  0,20  29,4  adequate  –  44(-2,-6)  -11,9  52,8   awropo11a-07  
E = sheep wool [0,041; R=26]
08   50,0  160,0  160,0  276,5  e=400
B=Polystyrene EPS-F [0,040] 
60  0,20  30,0  adequate  –  44(-2,-6)  -5,8  57,0   awropo11a-08  
E = glass wool [0,0040; R=16]
09   160,0  160,0  160,0  386,5  e=625
B=Polystyrene EPS-F [0,040] 
60  0,12  29,4  adequate  –  44(-2,-6)  7,5  54,6   awropo11a-09  
E = glass wool [0,0040; R=16]
10   50,0  160,0  160,0  276,5  e=625
B=Elasticized polystyrene FS 
60  0,19  29,4  adequate  –  47(-2,-6)  -5,5  52,8   awropo11a-10  
E = glass wool [0,0040; R=16]